Grey Cast Iron Properties

Delivery term:The date of payment from buyers deliver within days
  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Beijing

  • Validity to:

    Long-term effective

  • Last update:

    2019-05-20 17:07

  • Browse the number:

    275

Send an inquiries
Company Profile
Taizhou Jinzhiyuan Nodular Casting Co., Ltd.
Contactaixin:

tzjinzhiyuan(Mr.)  

Email:

telephone:

phone:

Arrea:

Beijing

Address:

No. 9 Binhai First Avenue, Togan Port Economic Development Zone, Linhai City, Zhejiang Province

Website:

http://www.jzyglobalcasting.com/ http://tzjinzhiyuan.zs-tongli.com/

Product details

Basic information

Material name: gray iron 200

Brand: HT200

Standard: GB/T 9439-2010

Refers to gray cast iron with a minimum tensile strength of 200MPa.

Hardness: 179~255HBS

 

Chemical composition

Carbon C: 3.16 ~ 3.30

Silicon Si: 1.79 ~ 1.93

Manganese Mn: 0.89 ~ 1.04

Sulfur S: 0.094 ~ 0.125

P: 0.120 ~ 0.170

 

Performance

Mechanical properties of

Tensile strength Rm (MPa) : 250

Hardness: (RH=1)209HB sample size: test bar diameter: 30mm

 

Other features

It has good strength [2], it’s resistant to abrasion and heat, possesses good vibration reduction, and excellent casting performance, which requires manual aging treatment.

 

Using range

Can be used for pump shells, containers, towers, flanges, packing box bodies and glands, carbonization towers, nitrification towers etc. Also employed in manufacturing, machine beds, columns, cylinders, gears and surface quenching parts.

Due to its resistance to deformation by heat, it is employed in high temperature environments.

 

Specification and organization

Heat treatment specification :(determined by the supplier, the following is the heat treatment specification for a sample for reference) in as-cast condition

Microstructure: flake graphite + pearlite

The HT250 can be quenched up to HRC60, but gray cast iron (HT200, HT250, etc.) is generally used in annealing or normalizing state without quenching. If hardness is required locally, high and medium frequency quenching is acceptable.

Medium frequency quenching: 3~5 mm hardening layer, hardness HRC50, the workpiece deformation is small.

High frequency quenching: 1~2 mm quenching layer, quenching temperature is 850, surface hardness HRC50 or above; Quenching temperature 900~1000 degrees, surface hardness up to HRC60.